POLYMER EXAMPLES MECHANICAL EXAMINATION AFTER ALKALINE SOLUTIONS PROCESSING

Avtandil Porchkhidze

doi:10.31435/rsglobal_ws/28022022/7783

POLYMER EXAMPLES MECHANICAL EXAMINATION AFTER ALKALINE SOLUTIONS PROCESSING

Avtandil Porchkhidze ассоциированный проф. академический доктор, Государственный университет Акакия Церетели, Грузия

DOI: https://doi.org/10.31435/rsglobal_ws/28022022/7783

Keywords: Polymer examples examination in alkaline environment after processing content tension was connected to deformation dependent. At the same time tension was rising up 10 mPa. Then was defined tension while was happening examples’ of quick disintegration.

Abstract

Polymer examples examination in alkaline environment after processing content tension was connected to deformation dependent. At the same time tension was rising up 10 mPa. Then was defined tension while was happening examples’ of quick disintegration.

References

Берштеин В.А. Дефеектность поверхностного слоя и прочность ориентированного полимера. Высокомолек. соед., 1978. Т.А. 20. Б 3. с. 579.

Моисеев Ю.В., Заиков Г.Е. Химическая стойкость полимеров в агрессивных средах. «Химия». М., 1979, с. 288.

Берштейн В.А., Егорова Л.М., Соловьев В.В. О разрушении полимеров по гидролитическому мехонизму, Высокомолек. Соед., 1977, Б. 5, с. 854-860.

Views:

165

Downloads:

Published

2022-02-16

Citations

How to Cite

Avtandil Porchkhidze. (2022). POLYMER EXAMPLES MECHANICAL EXAMINATION AFTER ALKALINE SOLUTIONS PROCESSING. World Science, (2(74). https://doi.org/10.31435/rsglobal_ws/28022022/7783

Download Citation

Issue

No 2(74) (2022): World Science

Section

Chemistry

This work is licensed under a Creative Commons Attribution 4.0 International License.

All articles are published in open-access and licensed under a Creative Commons Attribution 4.0 International License (CC BY 4.0). Hence, authors retain copyright to the content of the articles.
CC BY 4.0 License allows content to be copied, adapted, displayed, distributed, re-published or otherwise re-used for any purpose including for adaptation and commercial use provided the content is attributed.